Introduction
PRIMACOR™ 5986 Copolymer is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other substrates. It can be used effectively as a foil primer or laminating adhesive for polyethylene and metallized substrates.
PRIMACOR™ 5986 Copolymer exhibits:
· Low heat seal temperature, high hot tack
· High gloss, excellent clarity
· Excellent grease and oil resistance and excellent product resistance for flexible packaging applications
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
Resin | Density | 0.958 g/cm3 | 0.958 g/cm3 | ASTM D792 ISO 1183 |
Melt Index (2.16 kg @125℃)1 | 14 g/10min | 14 g/10min | ASTM D1238 | |
| Comonomer Content3 | 20.5 % | 20.5 % | SK Method | |
| Vicat Softening Temperature | 108 ℉ | 42.2 ℃ | ASTM D1525 ISO 306 | |
| Melting Temperature (DSC) | 171 ℉ | 77.2 ℃ | SK Method | |
Mechanical | Tensile Modulus-2% Secant | 4800 psi | 33.1 MPa | ASTM D638 |
Tensile Strength at Break | 1400 psi | 9.65 MPa | ASTM D638 ISO 527-2 | |
Tensile Elongation at Break (Compression Molded) | 390 % | 390 % | ASTM D638 ISO 527-2 | |
Durometer Hardness (Shore D) | 50 | 50 | ASTM D2240 ISO 868 |
1 As measured at the time of production.
2 Melt Index values are correlated from Melt Flow Rate (ASTM D 1238 conditions of 125℃/2.16 kg).
3 Comonomer content measured by a SK proprietary method that has equivalent accuracy as compared to ASTM D 4094.
Application
Ethylene and acrylic acid (EAA) copolymer resins offer excellent adhesion to polar substrates without the need for primers. Applications include liquid aseptic, dry-food and laminated tube container packaging, and cable shielding.
· Adhesives
· Laminations
· Foil priming
· Heat sealing
· Metal/paper coating
Extrusion Notes
Equipment used to process this resin should be constructed of corrosion resistant materials. Dies and adapters are
recommended to be stainless and/or duplex chrome or nickel plated.
Notes
These are typical values and are not be construed as specifications. The physical properties are highly dependent on the
manufacturing conditions. So customers should confirm performances by their own tests.