Introduction
ENGAGE™ 7447 is a high ethylene butene melt flow, low density copolymer designed for use alone or in combination with our other elastomers to provide the tailored solutions in polymer modifications applications.
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
Physical | Density | 0.865 g/cm3 | 0.865 g/cm3 | ASTM D792 |
Melt Index (190℃/2.16 kg ) | 5.0 g/10min | 5.0 g/10min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 250°F(121℃)) | 7 MU | 7 MU | ASTM D1646 | |
Mechanical | Tensile Modulus-100% Secant1 | 247 psi | 1.70 MPa | ASTM D638 |
Tensile Strength1 | 348 psi | 2.40 MPa | ASTM D638 | |
Tensile Elongation 1 (Break, Compression Molded) | 550 % | 550 % | ASTM D638 | |
Flexural Modulus 1% Secant : Compression Molded 2% Secant : Compression Molded | 1130 psi 1100 psi | 7.80 MPa 7.60 MPa | ASTM D790 | |
| Elastomers | Tear Strength 2 | 142 lbf/in | 24.8 kN/m | ASTM D624 |
| Hardness | Durometer Hardness Shore A, 1 sec, Compression Molded Shore D, 1 sec, Compression Molded | 64 12 | 64 12 | ASTM D2240 |
| Thermal | Glass Transition Temperature | -63.4 °F | -53.0 ℃ | Dow Method |
| Melting Temperature (DSC) 3 | 95.0 °F | 35.0 ℃ | Dow Method | |
| Peak Crystallization Temperature (DSC) | 84.2 °F | 29.0 ℃ | Dow Method |
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm resuits by their own tests.
1 20 in/min (510 mm/min)
2 Die C
3 10°C/min
Application
Polymer modification
Blends
Features
Pellet form
Low Density
Talc dusted (untreated,1μm)
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant