Introduction
ENGAGE™ 8003 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide variety of general purpose thermoplastic elastomer applications.
ENGAGE™ 8003 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE).
It also provides high filler loading capability and outstanding peroxide cure capability.
When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties, and may be used to produce high performance electrical insulation and jacketing.
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
Physical | Density | 0.885 g/cm3 | 0.885 g/cm3 | ASTM D792 |
Melt Index (190℃/2.16 kg ) | 1.0 g/10min | 1.0 g/10min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 250°F(121℃)) | 22 MU | 22 MU | ASTM D1646 | |
Mechanical | Tensile Modulus-100% Secant1 | 696 psi | 4.80 MPa | ASTM D638 |
Tensile Strength1 | 2640 psi | 18.2 MPa | ASTM D638 | |
Tensile Elongation 1 (Break, Compression Molded) | 640 % | 640 % | ASTM D638 | |
Flexural Modulus 1% Secant : Compression Molded 2% Secant : Compression Molded | 4890 psi 4730 psi | 33.7 MPa 32.6 MPa | ASTM D790 | |
| Elastomers | Tear Strength 2 | 348 lbf/in | 64.0 kN/m | ASTM D624 |
| Hardness | Durometer Hardness Shore A, 1 sec, Compression Molded Shore D, 1 sec, Compression Molded | 84 31 | 84 31 | ASTM D2240 |
| Thermal | Glass Transition Temperature | -50.8 °F | -46.0 ℃ | Dow Method |
| Vicat Softening Temperature | 145 °F | 63.0 ℃ | ASTM D1525 | |
| Melting Temperature (DSC) 3 | 171 °F | 77.0 ℃ | Dow Method | |
| Peak Crystallization Temperature (DSC) | 140 °F | 60.0 ℃ | Dow Method |
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm resuits by their own tests.
1 20 in/min (510 mm/min)
2 Die C
3 10°C/min
Application
General purpose thermoplastic elastomers
Wire and cable
Impact modification
Features
Pellet form
Excellent flow characteristics
Improved impact in polypropylene and polyethylene
High filler loading
Peroxide,silane,and radiation curable
Exceptional heat aging,compression set,and weather resistance
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant