Introduction
ENGAGE™ 8100 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications.
ENGAGE™ 8100 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE). ENGAGE 8100 provides high filler loading capability and outstanding peroxide cure capability.
When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties, and may be used to produce high performance electrical insulation.
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
Physical | Density | 0.870 g/cm3 | 0.870 g/cm3 | ASTM D792 |
Melt Index (190℃/2.16 kg ) | 1.0 g/10min | 1.0 g/10min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 250°F(121℃)) | 24 MU | 24 MU | ASTM D1646 | |
Mechanical | Tensile Modulus-100% Secant1 | 421 psi | 2.90 MPa | ASTM D638 |
Tensile Strength1 | 1420 psi | 9.76 MPa | ASTM D638 | |
Tensile Elongation 1 (Break, Compression Molded) | 810 % | 810 % | ASTM D638 | |
Flexural Modulus 1% Secant : Compression Molded 2% Secant : Compression Molded | 2070 psi 1900 psi | 14.3 MPa 13.1 MPa | ASTM D790 | |
| Elastomers | Tear Strength 2 | 228 lbf/in | 40.0 kN/m | ASTM D624 |
| Hardness | Durometer Hardness Shore A, 1 sec, Compression Molded Shore D, 1 sec, Compression Molded | 73 22 | 73 22 | ASTM D2240 |
| Thermal | Glass Transition Temperature | -61.6 °F | -52.0 ℃ | Dow Method |
| Vicat Softening Temperature | 113 °F | 45.0 ℃ | ASTM D1525 | |
| Melting Temperature (DSC) 3 | 140 °F | 60.0 ℃ | Dow Method | |
| Peak Crystallization Temperature (DSC) | 113 °F | 45.0 ℃ | Dow Method |
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm resuits by their own tests.
1 20 in/min (510 mm/min)
2 Die C
3 10°C/min
Application
General purpose thermoplastic elastomers
Wire and cable
Impact modification
Features
Pellet form
Excellent flow characteristics
Improved impact in polypropylene and polyethylene
High filler loading
Peroxide,silane,and radiation curable
Exceptional heat aging,compression set,and weather resistance when cured
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant