Introduction
ENGAGE™ 8150 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE) and is widely used in TPO applications where excellent low temperature impact properties are desired.
ENGAGE™ 8150 provides high filler loading capability and outstanding peroxide cure capability. When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties and may be used to produce high performance electrical insulation.
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
Physical | Density | 0.868 g/cm3 | 0.868 g/cm3 | ASTM D792 |
Melt Index (190℃/2.16 kg ) | 0.50 g/10min | 0.50 g/10min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 250°F(121℃)) | 33 MU | 33 MU | ASTM D1646 | |
Mechanical | Tensile Modulus-100% Secant1 | 377 psi | 2.60 MPa | ASTM D638 |
Tensile Strength1 | 1380 psi | 9.50 MPa | ASTM D638 | |
Tensile Elongation 1 (Break, Compression Molded) | 810 % | 810 % | ASTM D638 | |
Flexural Modulus 1% Secant : Compression Molded 2% Secant : Compression Molded | 2200 psi 2090 psi | 15.2 MPa 14.4 MPa | ASTM D790 | |
| Elastomers | Tear Strength 2 | 213 lbf/in | 37.3 kN/m | ASTM D624 |
| Hardness | Durometer Hardness Shore A, 1 sec, Compression Molded Shore D, 1 sec, Compression Molded | 70 20 | 70 20 | ASTM D2240 |
| Thermal | Glass Transition Temperature | -61.6 °F | -52.0 ℃ | Dow Method |
| Vicat Softening Temperature | 115 °F | 46.0 ℃ | ASTM D1525 | |
| Melting Temperature (DSC) 3 | 131 °F | 55.0 ℃ | Dow Method | |
| Peak Crystallization Temperature (DSC) | 108 °F | 42.0 ℃ | Dow Method |
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm resuits by their own tests.
1 20 in/min (510 mm/min)
2 Die C
3 10°C/min
Application
General purpose thermoplastic elastomers
Impact modification
Thermoplastic olefins (TPO)
Wire and cable
Features
Pellet form
Excellent flow characteristics
Improved impact in polypropylene and polyethylene
High filler loading
Peroxide,silane,and radiation curable
Exceptional heat aging,compression set,and weather resistance when cured
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant