Introduction
ENGAGE ™ 8400 Polyolefin Elastomer is an ethylene-octene copolymer that offers excellent performance in durableinjection molded industrial and consumer goods and compression molded gaskets.
ENGAGE ™ 8400 provides high clarity in products requiring visual inspection and allows the use of hot runner molds toenhance production efficiency.
In addition,the low density can help control resin and production costs,while reducingthe weight of end products.
ENGAGE ™8400 also provides good impact properties in blends with polypropylene (PP)and polyethylene (PE),especially in applications requiring high melt flow modifiers.
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
Physical | Density | 0.870 g/cm3 | 0.870 g/cm3 | ASTM D792 |
Melt Index (190℃/2.16 kg ) | 30 g/10min | 30 g/10min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 250°F(121℃)) | 2 MU | 2 MU | ASTM D1646 | |
Tensile Strength1 | 479 psi | 3.30 MPa | ASTM D638 | |
Tensile Elongation 1 (Break, Compression Molded) | 1000 % | 1000 % | ASTM D638 | |
Flexural Modulus 2% Secant : Compression Molded | 1750 psi | 12.1 MPa | ASTM D790 | |
| Hardness | Durometer Hardness Shore A, 1 sec, Compression Molded Shore D, 1 sec, Compression Molded | 72 20 | 72 20 | ASTM D2240 |
| Thermal | Glass Transition Temperature | -65.2 °F | -54.0 ℃ | Dow Method |
| Vicat Softening Temperature | 106 °F | 41.0 ℃ | ASTM D1525 | |
| Melting Temperature (DSC) 2 | 140 °F | 60.0 ℃ | Dow Method |
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm resuits by their own tests.
1 20 in/min (510 mm/min)
2 10°C/min
Application
Injection molded industrial and consumer durable goods
Impact modification
Features
Pellet form
Excellent flow characteristics
Improved impact in polypropylene and polyethylene
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant