Introduction
ENGAGE ™ 8440 Polyolefin Elastomer is an ethylene-octene copolymer that performs well in a wide range ofthermoplastic elastomer applications.It is an excellent thermoplastic elastomer for blending and compounding.
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
Physical | Density | 0.897 g/cm3 | 0.897 g/cm3 | ASTM D792 |
Melt Index (190℃/2.16 kg ) | 1.6 g/10min | 1.6 g/10min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 250°F(121℃)) | 13 MU | 13 MU | ASTM D1646 | |
Mechanical | Tensile Modulus-100% Secant1 | 914 psi | 6.30 MPa | ASTM D638 |
Tensile Strength1 | 2960 psi | 20.4 MPa | ASTM D638 | |
Tensile Elongation 1 (Break, Compression Molded) | 690 % | 690 % | ASTM D638 | |
Flexural Modulus 1% Secant : Compression Molded 2% Secant : Compression Molded | 7860 psi 7880 psi | 54.2 MPa 54.3 MPa | ASTM D790 | |
| Elastomers | Tear Strength 2 | 451 lbf/in | 78.9 kN/m | ASTM D624 |
| Hardness | Durometer Hardness Shore A, 1 sec, Compression Molded Shore D, 1 sec, Compression Molded | 86 36 | 86 36 | ASTM D2240 |
| Thermal | Glass Transition Temperature | -27.4 °F | -33.0 ℃ | Dow Method |
| Vicat Softening Temperature | 167 °F | 75.0 ℃ | ASTM D1525 | |
| Melting Temperature (DSC) 3 | 199 °F | 93.0 ℃ | Dow Method | |
| Peak Crystallization Temperature (DSC) | 169 °F | 76.0 ℃ | Dow Method |
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm resuits by their own tests.
1 20 in/min (510 mm/min)
2 Die C
3 10°C/min
Application
Thermoplastic elastomers
Compounding
Features
Pellet form
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant