Introduction
EXACT ™ 5061 plastomer resin is an ethylene 1-octene copolymerproduced using a proprietary metallocene technology.
It exhibitsoutstanding plastic and elastomeric properties including superior toughness.
EXACT ™ 5061 is designed for modification of polypropyleneand polyethylene in a wide range of applications such as injectionmolding, extrusion blow molding, blown and cast film, and profile extrusion.
Parameters
| General | Avalability 1 | Africa & Middle East, Europe, | ||
| Applications | Compounding and TPO Genearal purpose elastomer | |||
| Form (s) | Pellets | |||
| Revision Date | 04/01/2021 | |||
| Nominal Value (English) | Nominal Value (SI) | Test Based On | ||
Physical | Density | 0.868 g/cm3 | 0.868 g/cm3 | ASTM D1505 |
Melt Index (190℃/2.16 kg ) | 0.50 g/10min | 0.50 g/10min | ASTM D1238 | |
| Melt Mas-Flow Rate (MFR)(230℃/2.16kg) | 1.2 g/10min | 1.2 g/10min | ASTM 1238 | |
| Hardness | Durometer Hardness Shore A Shore D | 70 19 | 70 19 | ExxonMobil Method |
| Mechanical | Tensile Stress 2 | ＞ 1500 psi | ＞10 MPa | ExxonMobil Method |
| Tensile Stress at 100% (73°F(23℃)) | 360 psi | 2.5 MPa | ExxonMobil Method | |
| Elongation at Break 2 | ＞ 800 % | ＞ 800 % | ExxonMobil Method | |
| FlexuralMdiulus -1% Secant | 1800 psi | 13 MPa | ExxonMobil Method | |
| Elastomers | Tensile Strss at 300%(73℉(23℃)) | 508 psi | 3.50 MPa | ExxonMobil Method |
| Tear Strength(Die C) | 211 lbf/in | 37.0 kN/m | ExxonMobil Method | |
| Mooney Viscosity(ML 1+4, 257℉(125℃)) | 27 MU | 27 MU | ExxonMobil Method | |
| Thermal | Vicat Softening Temperature | 132 °F | 55.5 ℃ | ExxonMobil Method |
| Peak Melting Temperature | 127 °F | 53 ℃ | ExxonMobil Method | |
Additional | This product is talc dusted. | |||
Notes
Typical propeties: these are not to be construed as specifications.
1 Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
2 All specimens reached extension limit, did not break.
Application
Injection molded industrial and consumer durable goods
Impact modification of TPO
Features
Premium low temperature impact modifier
Free-flowing pellets
Superior toughness and tear strength
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant