Introduction
Exact 9071 is an ethylene butene copolymer produced using
ExxonMobil's proprietary metallocene catalyst technology.
This resin iscompatible with polyolefins like polypropylene (PP), polyethylene (PE)and ethylene-vinyl acetate copolymer resin (EVA).
Parameters
| General | Avalability 1 | Asia Pacific | ||
| Revision Date | 04/01/2017 | |||
| Nominal Value (English) | Nominal Value (SI) | Test Based On | ||
Physical | Density 2 | 0.870 g/cm3 | 0.870 g/cm3 | ExxonMobil Method |
Melt Index (190℃/2.16 kg ) | 0.5 g/10min | 0.5 g/10min | ExxonMobil Method | |
| Hardness | Durometer Hardness (Shore A ) | 71 | 71 | ASTM D2240 |
| Mechanical | FlexuralMdiulus -1% Secant | 2120 psi | 14.6 MPa | ASTM D790 |
| Elastomers | Tensile Strss at 100% | 460 psi | 3.17 MPa | ASTM D412 |
| Tensile Strength at Break | 747 psi | 5.15 MPa | ASTM D412 | |
| Elongation at Break | 480 % | 480% | ASTM D412 | |
| Thermal | Vicat Softening Temperature | 129 °F | 53.7 ℃ | ExxonMobil Method |
| Peak Melting Temperature | 119 °F | 49 ℃ | ExxonMobil Method | |
| Crystallization Peak, Tc | 96 °F | 36 ℃ | ExxonMobil Method | |
Glass Transition Tg | -55 °F | -48 ℃ | ExxonMobil Method | |
Notes
Typical propeties: these are not to be construed as specifications.
1 Product may not be available in one or more countries in the identified Availability regions. Please contact your Sales Representative for complete Country Availability.
2 Property results are displayed in conventional unit of measure.
Application
Injection molded industrial and consumer durable goods
Impact modification of TPO
Features
EVA foam modification.
PP/TPO modification.
Low density.
Low crystallinity.
Free flowing pellets.
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant