Introduction
LUCENE™ LC175 is an ethylene-1-butene copolymer produced using LG Chem's metallocene polymerization catalyst and solution process technology.
LUCENE™ LC175 is an excellent impact modifier for plastics and offers unique
performance capabilities for compounded products.
Typical properties
| Characteristics | Test Method | Unit | Value | |
| Physical (1) | Density | ASTM D 1505 | g/cm3 | 0.870 |
| MFR(190℃，2.16kg) | ASTM D 1238 | g/10min | 1.1 | |
| Mooney Viscosity(ML 1+4@121℃) | ASTM D 1646 | MU | 18 | |
| Mechanical (2) | Tensile Strength at Break | ASTM D638(3) | Mpa | 4.4 |
| Elongation at Break | ASTM D638(3) | % | ＞ 900 | |
| Tear Strength | ASTM D624 | kN/m | 34 | |
| FlexuralModulus 1% Secant | ASTM D790 | Mpa | 12 | |
| Hardness | Shore hardness(Shore A) | ASTM D2240 | - | 63 |
| Therma | Melting Temperature | LG | ℃ | 42 |
| Glass Transition Temperature | LG | ℃ | -53 |
(1) The properties data in this table are typical values, and not guaranteed specification.
(2) Typical resin property values are measured on a standard compression molded specimens
(3) Speed of 500 mm/min.
Application
General purpose thermoplastic elastomer for polymer modification
Automotive interior/exterior, Shoe sole, Wire & Cable
Features
General purpose thermoplastic elastomer for polymer modification
Automotive interior/exterior
Shoe sole
Wire & Cable
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.5-$3 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant