Introduction
Solumer™ 875L is an ethylene-octene copolymer produced via Nexlene™ technology.
Solumer™ 875L performs well in a wide range of general purpose thermoplastic elastomer applications and has excellent flow characteristics.
Properties
| Typical Values | Unit | Test Method | ||
Physical Properties | Density | 0.868 | g/cm3 | ASTM D792 |
| Melt index (2.16 kg @190℃) | 5.0 | g/10min | ASTM D1238 | |
| Mooney viscosity (ML1+4 @ 121℃) | 8 | MU | ASTM D1646 | |
Mechanical Properties 1 | Tensile strength at break | 63 | kgf/cm2 | ASTM D6382 |
| Elongation at break | ＞1000 | % | ASTM D6382 | |
| Tensile modulus (100% Elongation) | 24 | kgf/cm2 | ASTM D6382 | |
| Flexural modulus (1% secant) | 110 | kgf/cm2 | ASTM D790 | |
| Tear strength (Type C) | 38 | kgf/cm2 | ASTM D624 | |
| Hardness Shore A (1 sec) Shore D (1 sec) | 66 17 | - - | ASTM D2240 ASTM D2240 | |
Thermal Properties | Melting temperature | 61 | ℃ | SK Method |
| Glass transition temperature | -53 | ℃ | SK Method |
1 Evaluated using compression molded sample
2 Crosshead speed: 500 mm/min
Application
General purpose thermoplastic elastomers
Wire and cable
Impact modification
Footwear