Overview
AFFINITY* PF 1140G Polyolefin Plastomer (POP) is produced via lNSITE* Technology. lt is an ethylene alpha-olefin resin designed to be used in a variety of demanding applications including fom-fill-seal packaging and fresh producebags. This resin has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion.
High performance blown film resin for flexible packaging
Excellent abuse resistance
Low temperature seal initiation
Excellent optics
Outstanding high oxygen transmission rates
Complies with:
U.S.FDA FCN 424
Canadian HPFP No Objections
EU. NO 10/2011
U.S.FDA-DMF
Consult the regulations for complete details.
Additive
Antiblock: No
Slip: No
Processing Aid: No
Properties
| Nominal Value(English) | Nominal Value(SI) | Test Method | ||
| Physical | Density | 0.897 g/cm3 | 0.897 g/cm3 | ASTM D792 |
| Melt index (190℃/2.16kg) | 1.6 g/10 min | 1.6 g/10 min | ASTM D1238 | |
| Films | Film Thickness - Tested | 2.0 mil | 51 μm | |
| Film Puncture Energy (2.0 mil(51 μm)) | 72.4 in · lb | 8.18 J | Dow Method | |
| Film Puncture Force (2.0 mil(51 μm)) | 18.8 lbf | 83.6 N | Dow Method | |
| Film Puncture Resistance (2.0 mil(51 μm)) | 245 ft · b/in3 | 20.3 J/cm3 | Dow Method | |
Secant Modulus 2% Secant, MD : 2.0 mil(51 μm) 2% Secant, TD : 2.0 mil(51 μm) | 10600 psi 10600 psi | 72.8 MPa 73.2 MPa | ASTM D882 | |
Tensile Strength MD: Yield, 2.0 mil(51 μm) TD: Yield, 2.0 mil(51 μm) MD: Break, 2.0 mil(51 μm) TD: Break, 2.0 mil(51 μm) | 840 psi 920 psi 7290 psi 5730 psi | 5.79 MPa 6.34 MPa 50.3 MPa 39.5MPa | ASTM D882 | |
Tensile Elongation MD: Break, 2.0 mil(51 μm) TD: Break, 2.0 mil(51 μm) | 690 % 700 % | 690 % 700 % | ASTM D882 | |
| Dart Drop Impact 2.0 mil(51 μm) | ＞ 850 g | ＞ 850 g | ASTM D1709B | |
Elmendorf Tear Strength1 MD : 2.0 mil(51 μm) TD : 2.0 mil(51 μm) | 470 g 620 g | 470 g 620 g | ASTM D1922 | |
Seal Initiation Temperature2 2.0 mil(51 μm) | 178 ℉ | 81.1 ℃ | Dow Method | |
| Thermal | Vicat Softening Temperature | 170 ℉ | 76.7 ℃ | ASTM D1525 |
| Melting Temperature (DSC) | 205 ℉ | 96.1 ℃ | Dow Method | |
| Optical | Gloss (20℃, 2.00 mil(50.8 μm)) | 134 | 134 | ASTM D2457 |
| Clarity (2.00 mil(50.8 μm) | 70.0 | 70.0 | ASTM D1746 | |
| Haze (2.00 mil(50.8 μm)) | 1.30 % | 1.30 % | ASTM D1003 | |
| Extrusion | Melt Temperature | 40.8 ℉ | 209 ℃ | |
| Extrusion Nptes | Fabrication Conditions For Blown Film Screw Size: 2.5 in.(63.5 mm); 24:1 L/D Screw Type: Sterlex, Single Flight Double Mix Die Gap: 70 mil (1.8 mm) Melt Temperature: 408°F(209°C) Output: 6 lb/hr/in. of die circumference Die Diameter: 6 in. Blow-Up Ratio: 2.5:1 Screw Speed: 50 rpm Frost Line Height: 25 in. (635mm) | |||
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm results by their own tests.
1Modified rectangular test specimen.
2Temperature at which 1 lb/in. (4.4 N/25.4 mm) heat seal strength is achieved.
Heat Seal Strengths, Topwave HT Tester 0.5 S dwell, 40 psi bar pressure, pull speed 10 in./min (250 mm/sec).
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.8-$3.2 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant