Overview
AFFINITY* PL 1850G Polvolefin Plastomer (POP) is produced via INSITE* Technology. lt is designed to provide blown and cast film products with low temperature sealability, excellent optics and good abuse resistance.
It has value as a sealant layer in multilayer film structures for dry and liquid packaging.
High performance sealant layer in flexible packaging
Excellent optics, low temperature seal initiation and abuse resistance
Complies with:
U.S. FDA FCN 424
Canadian HPFB No Objectin
EU, NO 102011
Consult the regulations for complete details.
Additive
Antiblock: No
Slip: No
Processing Aid: No
Properties
| Nominal Value(English) | Nominal Value(SI) | Test Method | ||
| Physical | Density | 0.902 g/cm3 | 0.902 g/cm3 | ASTM D792 |
| Melt index (190℃/2.16kg) | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 | |
| Films | Film Thickness - Tested | 0.80 mil | 20 μm | |
| Film Puncture Energy (0.80 mil(20 μm)) | 37.9 in · lb | 4.28 J | Dow Method | |
| Film Puncture Force (0.80 mil(20 μm)) | 10.7 lbf | 47.6 N | Dow Method | |
| Film Puncture Resistance (0.80 mil(20 μm)) | 380 ft · b/in3 | 31.4 J/cm3 | Dow Method | |
Secant Modulus 2% Secant, MD : 0.80 mil (20 μm) 2% Secant, TD : 0.80 mil (20 μm) | 15700 psi 16600 psi | 108 MPa 115 MPa | ASTM D882 | |
Tensile Strength MD: Yield, 0.80 mil (20 μm) TD: Yield, 0.80 mil (20 μm) MD: Break, 0.80 mil (20 μm) TD: Break, 0.80 mil (20 μm) | 1440 psi 790 psi 6470 psi 4320 psi | 9.93 MPa 5.45 MPa 44.6 MPa 29.8MPa | ASTM D882 | |
Tensile Elongation MD: Break, 0.80 mil (20 μm) TD: Break, 0.80 mil (20 μm) | 350 % 570 % | 350 % 570 % | ASTM D882 | |
| Dart Drop Impact 0.80 mil (20 μm) | ＞ 830 g | ＞ 830 g | ASTM D1709B | |
Elmendorf Tear Strength1 MD : 0.80 mil (20 μm) TD : 0.80 mil (20 μm) | 120 g 410 g | 120 g 410 g | ASTM D1922 | |
Seal Initiation Temperature2 0.80 mil (20 μm) | 201 ℉ | 93.9 ℃ | Dow Method | |
| Thermal | Vicat Softening Temperature | 185 ℉ | 85.0 ℃ | ASTM D1525 |
| Melting Temperature (DSC) | 208 ℉ | 98.0 ℃ | Dow Method | |
| Optical | Gloss (20℃, 0.80 mil (20.3 μm)) | 144 | 144 | ASTM D2457 |
| Haze (0.80 mil (20.3 μm)) | 0.700 % | 0.700 % | ASTM D1003 | |
| Extrusion | Melt Temperature | 525 ℉ | 274 ℃ | |
| Extrusion Nptes | Fabrication Conditions For Blown Film Screw Size: 3.5 in.(89 mm); 32:1 L/D Screw Speed: 10 rpm Screw Size: 2.5 in.(63.5 mm); 24:1 L/D Screw Speed: 27 rpm Screw Size: 2.0 in.(51 mm); 24:1 L/D Screw Speed: 46 rpm Screw Type: Sterlex, Single Flight with Maddock Mixer & Single Flight Die Gap: 20 mil (0.5 mm) Chill Roll Temperature: 70°F(21°C) Melt Temperature: 525°F(274°C) Output: 243 lb/hr Line Speed: 600 fpm(183 m/min) | |||
Notes
These are typical properties only and are not to be construed as specifications. Users should confim results by their own tests.
1Modified rectangular test specimen.
2Temperature at which 1 lb/in. (4.4 N/25.4 mm) heat seal strength is achieved.
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.8-$3.2 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant