Overview
AFFINITY* PL 1880G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is designed for a variety of demanding packaging applications, including high-speed form-fill-seal packaging.
This resin offers excellent ultimate hot tack strenath and low temperature seal initiaton, even through contamination in the package.
Low seal initiation temperature
Excellent hot tack strength
High performance sealant layer in flexible packaging
Complies with:
U.S. FDA FCN 424
U.S.FDA-DMF
U.S. USP 23
HPFB No Objection (with limitations)
EU, No 10/2011.
Japan Hygienic Olefin and Styrene lastics Association
Consult the regulations for complete details.
Additive
Antiblock: No
Slip: No
Processing Aid: No
Properties
| Nominal Value(English) | Nominal Value(SI) | Test Method | ||
| Physical | Density | 0.902 g/cm3 | 0.902 g/cm3 | ASTM D792 |
| Melt index (190℃/2.16kg) | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 | |
| Films | Film Thickness - Tested | 2.0 mil | 51 μm | |
| Film Puncture Energy (2.0 mil(51 μm)) | 78.0 in · lb | 8.81 J | Dow Method | |
| Film Puncture Force (2.0 mil(51 μm)) | 20.8 lbf | 92.5 N | Dow Method | |
| Film Puncture Resistance (2.0 mil(51 μm)) | 270 ft · b/in3 | 22.3 J/cm3 | Dow Method | |
Secant Modulus 2% Secant, MD : 2.0 mil (51 μm) 2% Secant, TD : 2.0 mil (51 μm) | 13300 psi 13400 psi | 91.7 MPa 92.4 MPa | ASTM D882 | |
Tensile Strength MD: Yield, 2.0 mil (51 μm) TD: Yield, 2.0 mil (51 μm) MD: Break, 2.0 mil (51 μm) TD: Break, 2.0 mil (51 μm) | 1050 psi 1000 psi 8500 psi 6480 psi | 7.24 MPa 6.89 MPa 58.6 MPa 44.7MPa | ASTM D882 | |
Tensile Elongation MD: Break, 2.0 mil (51 μm) TD: Break, 2.0 mil (51 μm) | 620 % 630 % | 620 % 630 % | ASTM D882 | |
| Dart Drop Impact 2.0 mil (51 μm) | ＞ 830 g | ＞ 830 g | ASTM D1709B | |
Elmendorf Tear Strength1 MD : 2.0 mil (51 μm) TD : 2.0 mil (51 μm) | 550 g 720 g | 550 g 720 g | ASTM D1922 | |
Seal Initiation Temperature2 2.0 mil (51 μm) | 185 ℉ | 85.0 ℃ | Dow Method | |
| Thermal | Vicat Softening Temperature | 187 ℉ | 86.0 ℃ | ASTM D1525 |
| Melting Temperature (DSC) | 210 ℉ | 99.0 ℃ | Dow Method | |
| Optical | Gloss (20℃, 2.00 mil (50.8 μm)) | 141 | 141 | ASTM D2457 |
| Clarity (2.00 mil (50.8 μm)) | 83.0 | 83.0 | ASTM D1746 | |
| Haze (2.00 mil (50.8 μm)) | 1.10 % | 1.10 % | ASTM D1003 | |
| Extrusion | Melt Temperature | 408 ℉ | 209 ℃ | |
| Extrusion Nptes | Fabrication Conditions For Blown Film Screw Size: 2.5 in. (63.5 mm); 24:1 L/D Screw Type: SFDM Die Gap: 70 mil (1.8 mm) Melt Temperature: 408°F(209°C) Output: 6 lb/hr/in. of die circumference Die Diameter: 6 in. Blow-Up Ratio: 2.5:1 Screw Speed: 50 rpm | |||
Notes
These are typical properties only and are not to be construed as specifications. Users should confim results by their own tests.
1Modified rectangular test specimen.
2Temperature at which 2 lb/in. (8.8 N/25.4 mm) heat seal strength is achieved.
Heat Seal Strengths, Topwave HT Tester 0.5 S dwell, 40 psi bar pressure, pull speed 10 in./min (250 mm/sec).
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.8-$3.2 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant