AFFINITY* PL 1881G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is designed for a variety of demanding packaging applications, including high-speed form-fill-seal products.
Excellent ultimate hot tack strength
Low temperature sealability
Ability to seal through contamination
Outstanding optics
Complies with:
U.S. FDA FCN 424
Canadian HPFB No Objection (with limitations)
EU, No 10/2011
Consult the regulations for complete details.
Additive
Antiblock: 2500ppm
Slip: 750 ppm
Properties
| Nominal Value(English) | Nominal Value(SI) | Test Method | ||
| Physical | Density | 0.904 g/cm3 | 0.904 g/cm3 | ASTM D792 |
| Melt index (190℃/2.16kg) | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 | |
| Mechanical | Coefficient of Friction vs. Itself - Dynamic | 0.15 | 0.15 | ASTM D18 |
| Films | Film Thickness - Tested | 2.0 mil | 51 μm | |
| Film Puncture Energy (2.0 mil(51 μm)) | 71.6 in · lb | 8.09 J | Dow Method | |
| Film Puncture Force (2.0 mil(51 μm)) | 18.5 lbf | 82.3 N | Dow Method | |
| Film Puncture Resistance (2.0 mil(51 μm)) | 265 ft · b/in3 | 21.9 J/cm3 | Dow Method | |
Secant Modulus 2% Secant, MD : 2.0 mil (51 μm) 2% Secant, TD : 2.0 mil (51 μm) | 14100 psi 14100 psi | 97.4 MPa 97.4 MPa | ASTM D882 | |
Tensile Strength MD: Yield, 2.0 mil (51 μm) TD: Yield, 2.0 mil (51 μm) MD: Break, 2.0 mil (51 μm) TD: Break, 2.0 mil (51 μm) | 1170 psi 1040 psi 6580 psi 6170 psi | 8.07 MPa 7.17 MPa 45.4 MPa 42.5MPa | ASTM D882 | |
Tensile Elongation MD: Break, 2.0 mil (51 μm) TD: Break, 2.0 mil (51 μm) | 590 % 630 % | 590 % 630 % | ASTM D882 | |
| Dart Drop Impact 2.0 mil (51 μm) | ＞ 830 g | ＞ 830 g | ASTM D1709B | |
Elmendorf Tear Strength1 MD : 2.0 mil (51 μm) TD : 2.0 mil (51 μm) | 560 g 730 g | 560 g 730 g | ASTM D1922 | |
Seal Initiation Temperature2 2.0 mil (51 μm) | 185 ℉ | 85.0 ℃ | Dow Method | |
| Block Force | 70 g | 70 g | ASTM D3354-89 | |
| Thermal | Vicat Softening Temperature | 187 ℉ | 86.0 ℃ | ASTM D1525 |
| Melting Temperature (DSC) | 212 ℉ | 100 ℃ | Dow Method | |
| Optical | Gloss (20℃, 2.00 mil (50.8 μm)) | 112 | 112 | ASTM D2457 |
| Clarity (2.00 mil (50.8 μm)) | 83.0 | 83.0 | ASTM D1746 | |
| Haze (2.00 mil (50.8 μm)) | 3.20 % | 3.20 % | ASTM D1003 | |
| Extrusion | Melt Temperature | 430 ℉ | 221 ℃ | |
| Extrusion Nptes | Fabrication Conditions For Blown Film Screw Size: 2.5 in. (63.5 mm); 24:1 L/D Screw Type: DSB ll Die Gap: 70 mil (1.8 mm) Melt Temperature: 430°F(221°C) Output: 6 lb/hr/in. of die circumference Die Diameter: 6 in. Blow-Up Ratio: 2.5:1 Screw Speed: 40 rpm | |||
Notes
These are typical properties only and are not to be construed as specifications. Users should confim results by their own tests.
1Modified rectangular test specimen.
2Temperature at which 2 lb/in. (8.8 N/25.4 mm) heat seal strength is achieved.
Heat Seal Strengths, Topwave HT Tester 0.5 S dwell, 40 psi bar pressure, pull speed 10 in./min (250 mm/sec).
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.8-$3.2 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant