Introduction
Supreme™ 028, Polyolefin Plastomer (POP) is an ethylene-octene copolymer produced via Nexlene™ technology. Supreme™ 028 performs well in a wide range of various cast film applications with excellent sealing property and impact strength.
Typical Performance:
Superior low seal initiation temperature and hot tack strength
Excellent impact strength and transparency
Properties
| Typical Values | Unit | Test Method | ||
| Physical Properties | Density | 0.902 | g/cm3 | ASTM D792 |
| Melt index (2.16kg @ 190℃) | 7.5 | g/10min | ASTM D1238 | |
| Melting temper ature | 96 | ℃ | SK Method | |
| Vicat softening temperature | 80 | ℃ | ASTM D1525 | |
| Film Properties | Film thickness-tested | 25 | μm | ASTM D374 |
| Dart impact strength | 500 | g | ASTM D1709A | |
| Haze | 0.5 | % | ASTM D1003 | |
| Seal initiation temperature | 84 | ℃ | SK Method1 | |
| Extrusion Condition | Screw size: 30 mm Screw speed: 30 rpm Die gap: 1 mm Melt temperature: 230℃ | |||
1 Temperature at which 0.4kg/25.4 mm heat seal strength is achieved
Notes
These are typical values and are not be construed as specifications. The physical properties are highly dependent on the manufacturing conditions. So customers should confirm performances by their own tests.
Applications
General purpose thermoplastic elastomers
Wire and cable
Impact modification
Footwear
Features
Supreme™ 028
Generic Family: Plastomer, Polyolefin
Supplied by: SK Geo Centric
Excellent low seal initiation temperature and hot tack strength Outstanding cling property Superior impact strength and transparency
Parameters
Minimum Order Quantity: | 25kg |
Price: | $1.8-$3.2 |
Packaging Details: | 25kg/bag |
Delivery Time: | 3-5 working days to departure port |
Payment Terms: | TT/LC |
Supply Ability: | 1000MT/Month |
Sales consultant